Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Advertisement
Nature Materials (2025)
7444
4
2
Metrics details
Efficient wide-bandgap perovskite solar cells have pushed tandem efficiencies to 34.9%, reinforcing their promise for next-generation photovoltaics. However, their commercial adoption is hindered by stability issues of wide-bandgap perovskites, especially under high-temperature maximum power point tracking conditions. Here we report the stabilization of ~1.7-eV wide-bandgap perovskites via intermediate phase evolution, enabling a self-guided crystal-growth mode. A CsI2Br intermediate phase forms during early stage deposition, directing the oriented growth of polycrystalline films with unique texturing. Atomic-scale scanning transmission electron microscopy reveals that the CsI2Br ((1bar{2}3)) facet, with a 2.9-Å interplanar spacing, matches the perovskite (200) facet, guiding coherent {100} growth. This results in enhanced crystallinity, with a 2-order-magnitude increase in the (100) diffraction intensity and a reduced full-width at half-maximum from 0.249° to 0.148°, compared with solution-processed films. The resulting solar cells exhibit outstanding thermal and operational stability, maintaining performance under maximum power point tracking for over 3,000 h at room temperature and over 500 h at 110 °C, with a projected lifetime of ~70,000 h. With 21.37% power conversion efficiency and >84% fill factor, this work presents a compelling route towards stable, high-efficiency tandem photovoltaics.
This is a preview of subscription content, access via your institution
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$32.99 / 30 days
cancel any time
Subscribe to this journal
Receive 12 print issues and online access
$259.00 per year
only $21.58 per issue
Buy this article
USD 39.95
Prices may be subject to local taxes which are calculated during checkout
The data supporting this study are included in the article and its Supplementary Information. Further information are available from the corresponding authors on request.
Ramadan, A. J., Oliver, R. D. J., Johnston, M. B. & Snaith, H. J. Methylammonium-free wide-bandgap metal halide perovskites for tandem photovoltaics. Nat. Rev. Mater. 8, 822–838 (2023).
Article CAS Google Scholar
Fu, F. et al. Monolithic perovskite-silicon tandem solar cells: from the lab to fab?. Adv. Mater. 34, 2106540 (2022).
Article CAS Google Scholar
Aydin, E. et al. Pathways toward commercial perovskite/silicon tandem photovoltaics. Science 383, eadh3849 (2024).
Article CAS PubMed Google Scholar
Li, H. & Zhang, W. Perovskite tandem solar cells: from fundamentals to commercial deployment. Chem. Rev. 120, 9835–9950 (2020).
Article CAS PubMed Google Scholar
Duan, L. et al. Stability challenges for the commercialization of perovskite–silicon tandem solar cells. Nat. Rev. Mater. 8, 261–281 (2023).
Article CAS Google Scholar
Cheng, Y. & Ding, L. Perovskite/Si tandem solar cells: fundamentals, advances, challenges, and novel applications. SusMat 1, 324–344 (2021).
Article CAS Google Scholar
Ji, X. et al. Multifunctional buffer layer engineering for efficient and stable wide-bandgap perovskite and perovskite/silicon tandem solar cells. Angew. Chem. Int. Ed. 136, e202407766 (2024).
Article Google Scholar
Liu, J. et al. Efficient and stable perovskite-silicon tandem solar cells through contact displacement by MgFx. Science 377, 302–306 (2022).
Article CAS PubMed Google Scholar
Khadka, D. B. et al. Defect passivation in methylammonium/bromine free inverted perovskite solar cells using charge-modulated molecular bonding. Nat. Commun. 15, 882 (2024).
Article CAS PubMed PubMed Central Google Scholar
Ye, Q. et al. Suppressing charge recombination in a methylammonium-free wide-bandgap perovskite film for high-performance and stable perovskite solar cells. Energy Environ. Sci. 17, 5866–5875 (2024).
Article CAS Google Scholar
Chen, S. et al. Crystallization in one-step solution deposition of perovskite films: upward or downward?. Sci. Adv. 7, eabb2412 (2021).
Article CAS PubMed PubMed Central Google Scholar
Zhang, H. et al. Controllable heterogenous seeding-induced crystallization for high-efficiency FAPbI3-based perovskite solar cells over 24%. Adv. Mater. 34, 2204366 (2022).
Article CAS Google Scholar
Kim, H.-S., Seo, J.-Y. & Park, N.-G. Material and device stability in perovskite solar cells. ChemSusChem 9, 2528–2540 (2016).
Article CAS PubMed Google Scholar
Ma, C. et al. Photovoltaically top-performing perovskite crystal facets. Joule 6, 2626–2643 (2022).
Article CAS Google Scholar
Li, X. et al. Bifunctional ligand-induced preferred crystal orientation enables highly efficient perovskite solar cells. Joule 8, 3169–3185 (2024).
Article CAS Google Scholar
Zhao, W. et al. Orientation engineering via 2D seeding for stable 24.83% efficiency perovskite solar cells. Adv. Energy Mater. 13, 2204260 (2023).
Article CAS Google Scholar
Jiang, X. et al. Top-down induced crystallization orientation toward highly efficient p-i-n perovskite solar cells. Adv. Mater. 36, 2313524 (2024).
Article CAS Google Scholar
Luo, C. et al. Facet orientation tailoring via 2D-seed-induced growth enables highly efficient and stable perovskite solar cells. Joule 6, 240–257 (2022).
Article CAS Google Scholar
Wang, T. et al. 2D WSe2 flakes for synergistic modulation of grain growth and charge transfer in tin-based perovskite solar cells. Adv. Sci. 8, 2004315 (2021).
Article CAS Google Scholar
Cao, J. et al. Enhanced performance of planar perovskite solar cells induced by van der Waals epitaxial growth of mixed perovskite films on WS2 flakes. Adv. Funct. Mater. 30, 2002358 (2020).
Article CAS Google Scholar
Li, S. et al. Coherent growth of high-Miller-index facets enhances perovskite solar cells. Nature 635, 874–881 (2024).
Article PubMed Google Scholar
Abzieher, T. et al. Vapor phase deposition of perovskite photovoltaics: short track to commercialization?. Energy Environ. Sci. 17, 1645–1663 (2024).
Article Google Scholar
Li, H. et al. Applications of vacuum vapor deposition for perovskite solar cells: a progress review. iEnergy 1, 434–452 (2022).
Article Google Scholar
Kosasih, F. U., Erdenebileg, E., Mathews, N., Mhaisalkar, S. G. & Bruno, A. Thermal evaporation and hybrid deposition of perovskite solar cells and mini-modules. Joule 6, 2692–2734 (2022).
Article CAS Google Scholar
Vaynzof, Y. The future of perovskite photovoltaics—thermal evaporation or solution processing?. Adv. Energy Mater. 10, 2003073 (2020).
Article CAS Google Scholar
Kim, B.-S., Gil-Escrig, L., Sessolo, M. & Bolink, H. J. Deposition kinetics and compositional control of vacuum-processed CH3NH3PbI3 perovskite. J. Phys. Chem. Lett. 11, 6852–6859 (2020).
Article CAS PubMed Google Scholar
Kaya, I. C. et al. Crystal reorientation and amorphization induced by stressing efficient and stable P–I–N vacuum-processed MAPbI3 perovskite solar cells. Adv. Energy Sustain. Res. 2, 2000065 (2021).
Article CAS Google Scholar
Wang, Z. et al. Efficient ambient-air-stable solar cells with 2D–3D heterostructured butylammonium-caesium-formamidinium lead halide perovskites. Nat. Energy 2, 17135 (2017).
CAS Google Scholar
Fu, J. A general approach to determine texture patterns using pole figure. J. Mater. Res. Technol. 14, 1284–1291 (2021).
Article CAS Google Scholar
Luo, J. et al. Vapour-deposited perovskite light-emitting diodes. Nat. Rev. Mater. 9, 282–294 (2024).
Article CAS Google Scholar
Li, J. et al. Efficient all-thermally evaporated perovskite light-emitting diodes for active-matrix displays. Nat. Photon. 17, 435–441 (2023).
Article CAS Google Scholar
Jain, A. et al. Commentary: The Materials Project: a materials genome approach to accelerating materials innovation. APL Mater. 1, 011002 (2013).
Article Google Scholar
Carpenter, G. B. The crystal structure of CsI2Br. Acta Cryst. 20, 330–334 (1966).
Article CAS Google Scholar
Darwent, B. d. Bond Dissociation Energies in Simple Molecules (National Bureau of Standards, 1970).
Chen, Z. et al. Thermal stability and decomposition kinetics of mixed-cation halide perovskites. Phys. Chem. Chem. Phys. 25, 32966–32971 (2023).
Article CAS PubMed Google Scholar
Tay, D. J. J. et al. Understanding the mechanisms of methylammonium-induced thermal instability in mixed-FAMA perovskites. Small 21, 2403389 (2025).
Article CAS Google Scholar
Zhuang, J., Wang, J. & Yan, F. Review on chemical stability of lead halide perovskite solar cells. Nano-Micro Lett. 15, 84 (2023).
Article CAS Google Scholar
Francisco-López, A. et al. Phase diagram of methylammonium/formamidinium lead iodide perovskite solid solutions from temperature-dependent photoluminescence and Raman spectroscopies. J. Phys. Chem. C 124, 3448–3458 (2020).
Article Google Scholar
Zhou, Y., Poli, I., Meggiolaro, D., De Angelis, F. & Petrozza, A. Defect activity in metal halide perovskites with wide and narrow bandgap. Nat. Rev. Mater. 6, 986–1002 (2021).
Article Google Scholar
Long, M. et al. Abnormal synergetic effect of organic and halide ions on the stability and optoelectronic properties of a mixed perovskite via in situ characterizations. Adv. Mater. 30, 1801562 (2018).
Article Google Scholar
LaFollette, D. K. et al. Bromine incorporation affects phase transformations and thermal stability of lead halide perovskites. J. Am. Chem. Soc. 146, 18576–18585 (2024).
Article CAS PubMed PubMed Central Google Scholar
Steele, J. A. et al. How to GIWAXS: grazing incidence wide angle X-ray scattering applied to metal halide perovskite thin films. Adv. Energy Mater. 13, 2300760 (2023).
Article CAS Google Scholar
Saha, R. A. et al. Oxygen-mediated (0D) Cs4PbX6 formation during open-air thermal processing improves inorganic perovskite solar cell performance. ACS Nano 18, 16994–17006 (2024).
Article CAS PubMed Google Scholar
Khanna, Y. P. & Taylor, T. J. Comments and recommendations on the use of the Avrami equation for physico-chemical kinetics. Polym. Eng. Sci. 28, 1042–1045 (1988).
Article CAS Google Scholar
Thiesbrummel, J. et al. Ion-induced field screening as a dominant factor in perovskite solar cell operational stability. Nat. Energy 9, 664–676 (2024).
Article CAS Google Scholar
Khenkin, M. V. et al. Consensus statement for stability assessment and reporting for perovskite photovoltaics based on ISOS procedures. Nat. Energy 5, 35–49 (2020).
Article Google Scholar
Zhao, X. et al. Accelerated aging of all-inorganic, interface-stabilized perovskite solar cells. Science 377, 307–310 (2022).
Article CAS PubMed Google Scholar
Burlingame, Q. et al. Intrinsically stable organic solar cells under high-intensity illumination. Nature 573, 394–397 (2019).
Article CAS PubMed Google Scholar
Li, Y. et al. Non-fullerene acceptor organic photovoltaics with intrinsic operational lifetimes over 30 years. Nat. Commun. 12, 5419 (2021).
Article CAS PubMed PubMed Central Google Scholar
Haillant, O., Dumbleton, D. & Zielnik, A. An Arrhenius approach to estimating organic photovoltaic module weathering acceleration factors. Sol. Energy Mater. Sol. Cells 95, 1889–1895 (2011).
Article CAS Google Scholar
Kettle, J. et al. Using ISOS consensus test protocols for development of quantitative life test models in ageing of organic solar cells. Sol. Energy Mater. Sol. Cells 167, 53–59 (2017).
Article CAS Google Scholar
Zhao, X. et al. Operationally stable perovskite solar modules enabled by vapor-phase fluoride treatment. Science 385, 433–438 (2024).
Article CAS PubMed Google Scholar
Jiang, Q. et al. Towards linking lab and field lifetimes of perovskite solar cells. Nature 623, 313–318 (2023).
Article CAS PubMed Google Scholar
Khenkin, M. & Albrecht, S. The way to predict outdoor lifetime. Nat. Energy 9, 12–13 (2024).
Article Google Scholar
National Solar Radiation Database (NSRDB, 2024); https://nsrdb.nrel.gov/
What is the potential of solar energy in Singapore? Energy Market Authority of Singapore https://www.ema.gov.sg/resources/faqs/energy-supply/solar/what-is-the-potential-of-solar-energy-in-singapore (2023).
Chen, W. et al. Monolithic perovskite/organic tandem solar cells with 23.6% efficiency enabled by reduced voltage losses and optimized interconnecting layer. Nat. Energy 7, 229–237 (2022).
Article CAS Google Scholar
Ashiotis, G. et al. The fast azimuthal integration Python library: pyFAI. J. Appl. Cryst. 48, 510–519 (2015).
Article CAS Google Scholar
Perdew, J. P. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Article CAS PubMed Google Scholar
Kresse, G. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Article CAS Google Scholar
Download references
Y.H. acknowledges support from the Agency for Science, Technology and Research (A*STAR) under its MTC IRG Grant (M23M6c0108). We are affiliated with the Solar Energy Research Institute of Singapore (SERIS), a research institute at the National University of Singapore (NUS). SERIS is supported by the NUS, the National Research Foundation Singapore (NRF), the Energy Market Authority of Singapore (EMA) and the Singapore Economic Development Board (EDB). We acknowledge that computational work involved in this research work is fully supported by NUS IT’s Research Computing group under grant number NUSREC-HPC-00001. J.A.S. acknowledges financial support from the Australian Research Council (DE230100173). We thank the staff of the BL11 NCD-SWEET beamline at ALBA Synchrotron for their assistance in recording the GIWAXS data.
These authors contributed equally: Zijing Dong, Jingcong Hu, Xiao Guo.
Department of Chemical and Biomolecular Engineering, National University of Singapore, Singapore, Singapore
Zijing Dong, Jingcong Hu, Xiao Guo, Zhuojie Shi, Ran Luo, Qilin Zhou, Nengxu Li, Tao Wang, Jinxi Chen, Yuduan Wang, Jia Li & Yi Hou
Solar Energy Research Institute of Singapore (SERIS), National University of Singapore, Singapore, Singapore
Zijing Dong, Xiao Guo, Zhuojie Shi, Ran Luo, Qilin Zhou, Nengxu Li, Tao Wang, Jinxi Chen, Ling Kai Lee, Yuduan Wang, Jia Li & Yi Hou
State Key Laboratory of Materials Low-Carbon Recycling, Beijing University of Technology, Beijing, China
Jingcong Hu, Manling Sui & Yue Lu
State Key Laboratory of Advanced Fiber Materials, Institute of Functional Materials, College of Materials Science and Engineering, Donghua University, Shanghai, China
Haijie Chen & Yunluo Wang
Australian Institute for Bioengineering and Nanotechnology, The University of Queensland, St Lucia, Queensland, Australia
Julian A. Steele
School of Mathematics and Physics, The University of Queensland, St Lucia, Queensland, Australia
Julian A. Steele & Zachary Degnan
NCD-SWEET beamline, ALBA Synchrotron Light Source, Cerdanyola del Vallès, Spain
Eduardo Solano
Electronic Engineering Department, The Chinese University of Hong Kong, Hong Kong SAR, China
Nikhil Kalasariya & Martin Stolterfoht
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
PubMed Google Scholar
Z. Dong and Y.H. conceived the idea and designed the experiments. Y.H. directed and supervised the project. Z. Dong fabricated the PSCs and conducted stability tests under accelerated aging. J.H., Y.L. and M. Sui conducted the STEM characterization and data analysis. Z. Dong and X.G. investigated the thermal degradation mechanisms and conducted the material and device characterizations. Z.S. helped with the XRD measurement. Q.Z., T.W. and L.K.L. helped with the device fabrication. J.A.S., Z. Degnan and E.S. performed the in situ GIWAXS measurements. H.C. and Yunluo Wang helped with the pole figure measurements. R.L. contributed to the DFT simulations. J.C. helped with the XPS measurements. N.K. and M. Stolterfoht helped with the bias-assisted charge extraction measurement. J.L., N.L. and Yuduan Wang helped with the thermal evaporation of perovskite films. Z. Dong and Y.H. analysed the results and composed the paper. All authors discussed and polished the paper.
Correspondence to Yue Lu or Yi Hou.
Y.H. is the founder of Singfilm Solar, a company commercializing perovskite photovoltaics. The other authors declare no competing interests.
Nature Materials thanks Shangfeng Yang and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Figs. 1–27, Tables 1–6 and Notes 1–4.
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
Reprints and permissions
Dong, Z., Hu, J., Guo, X. et al. Intermediate phase evolution for stable and oriented evaporated wide-bandgap perovskite solar cells. Nat. Mater. (2025). https://doi.org/10.1038/s41563-025-02375-8
Download citation
Received:
Accepted:
Published:
Version of record:
DOI: https://doi.org/10.1038/s41563-025-02375-8
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
Nature Materials (2025)
Advertisement
Nature Materials (Nat. Mater.)
ISSN 1476-4660 (online)
ISSN 1476-1122 (print)
© 2026 Springer Nature Limited
Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.